HYSOFIX 701 Cyanoacrylate Glue - 20gHYSOFIX 701 is a new generation triple distillation glue. Adhesive based on modified methylcyanoacrylate intended for joining a wide group of materials: metal, wood, porcelain, glass, ceramics, rubber, PVC (gluing tarpaulins). , banners) and other materials and combinations of these materials.

Adhesive particularly suitable for joining small parts.

The adhesive has good fatigue resistance, very high shear and tensile strength.

How to use the glue correctly?Glued parts should be joined quickly , because the shelf life of the adhesive is very short.

Air humidity is generally sufficient to initiate curing in a few seconds and obtain manual strength (full mechanical strength and chemical resistance is achieved only after 24 hours).

The best results are obtained at relative humidity air 40-60%.

Activators should be used to speed up the polymerization and hardening process.

The size of the gap also has a significant impact on the speed of hardening (the larger the gap, the slower the glue sets) and the type of glued materials.

Setting time PVC 2-15

phenolic resins 10-20

ABS polymers 5-10

steel 10-20

aluminum 5-15

zinc 30-90

chloroprene or nitrile rubber <,10<,/strong>,

Typical product properties . uncuredChemical type: modified ethylcyanoacrylic

Color: colorless

Viscosity: 100-150 [mPa.s] at 20°C

Specific gravity: 1.05 [g/ml] at 20°C

Flash point (ISO 2592 ): >,80°C

Solvent content: none

Storage: up to 12 months at 8-28°C

Properties of the hardened product (after 24 hours)Join gap [m]: 10-100

Tensile strength [ N/mm2]: 22-25

Wall strength [N/mm2]: 13-22

Impact strength [Nxmm/mm2]: 13-18

Operating temperature range: - 50 +90°C

Temp . softening +160/170°C

Coefficient refraction [nd20]: similar to glass

Specific resistance [Ω x mm]: 10

Breakdown voltage [kV/mm]: 12-13

Dielectric constant [1MHz]: 5.2

Preparation:The elements to be joined should be thoroughly clean the remnants of old glue and degrease well, preferably with REINIGER remover. HYSOFIX 701 glue should be applied sparingly to one of the glued surfaces and quickly press the bonded parts.

When bonding non-bondable materials (polyolefins), the surface of the material should be activated with AKTYWATOR C.

The glue itself can be activated with AKTYWATOR C, which accelerates the action of the glue. and hardens its excess. We use the activator to moisten the glue in the joint or to moisten the joint surfaces before gluing and after it dries, we glue.

The activation process can be repeated many times by applying subsequent layers of glue. In this way, you can obtain a thick joint (as in the case of epoxy resins) with high hardness, mechanical strength and a very short setting time.

It is not recommended to use this product for devices with pure oxygen, chlorine or other strongly oxidizing substances.

ParametersWarranty: 24 months

Capacity: 20 ml

Weight: 0.03 kg

product_code: 0036

model: HYSOFIX 701 Cyanoacrylate Adhesive - 20g

dominant color: Transparent

type: Cyanoacrylic

type: Adhesive