Hysofix 701 cyanoacrylate glue 50g

HYSOFIX 701 Cyanoacrylate Glue - 50g LEPRO

HYSOFIX 701 Cyanoacrylate Glue - 50gHYSOFIX 701 This is a new generation triple distillation glue.

Adhesive based on modified methylcyanoacrylate intended for joining a wide group of materials: metal, wood, porcelain, glass, ceramics, rubber, cork, paper, stone, PVC (gluing tarpaulins, banners) and other materials and combinations of these materials.

Adhesive particularly suitable for connecting small parts.

The glue has good fatigue resistance, very high shear and tensile strength

How to use the glue correctly? Glued parts must be joined quickly because the shelf life of the glue is very short.

Air humidity is generally sufficient to initiate curing in a few seconds and obtain manual strength (full mechanical strength and chemical resistance is achieved only after 24 hours).

The best results are obtained at a relative air humidity of 40-60%.

To accelerate the polymerization process and hardening, activators should be used.

The size of the gap also has a significant impact on the speed of hardening (the larger the gap, the slower the glue hardens) and the type of glued materials.

PVC setting time 2-15

phenolic resins 10-20

ABS polymers 5-10

steel 10-20

aluminum 5-15

zinc 30-90

chloroprene or nitrile rubber <,10

Typical product properties uncured Chemical type: modified ethylcyanoacrylic

Color: colorless

Viscosity: 100-150 [mPa.s] at 20°C

Specific gravity: 1.05 [g/ml] at 20°C

Flash point (ISO) 2592): >.80°C

Solvent content: none

Storage: up to 12 months at 8-28°C

Properties of the hardened product (after 24 hours) Joint gap [m]: 10-100

Tensile strength [N/mm2]: 22-25

Wall strength [N/mm2]: 13-22

Impact strength [Nxmm/mm2]: 13-18

Operating temperature range: - 50 +90°C

Temp. softening +160/170°C

Coefficient refraction [nd20]: similar to glass

Specific resistance [Ω x mm]: 10

Breakdown voltage [kV/mm]: 12-13

Dielectric constant [1MHz]: 5.2

Preparation: Connected elements should be thoroughly clean the remnants of old glue and degrease well, preferably with REINIGER remover. HYSOFIX 701 glue should be applied sparingly to one of the glued surfaces and quickly press the bonded parts.

When bonding non-bondable materials (polyolefins), the surface of the material should be activated with AKTYWATOR C.

The glue itself can be activated with AKTYWATOR C, which accelerates the action of the glue. and hardens its excess. We use the activator to moisten the glue in the joint or to moisten the joint surfaces before gluing and after it dries, we glue.

The activation process can be repeated many times by applying subsequent layers of glue. In this way, you can obtain a thick joint (as in the case of epoxy resins) with high hardness, mechanical strength and a very short setting time.

It is not recommended to use this product for devices with pure oxygen, chlorine or other strongly oxidizing substances.

Condition: New

Type: other

Intended use: universal

Capacity: 50

Brand: Lepro

Application: indoors

Packaging: Bottle

Setting time: quick-drying

Features: flexible

Curing: at ambient temperature

Color: transparent

EAN (GTIN): 6096320450452

Manufacturer's code: MEGA HYSOFIX FIX 701 CYANOACRYLATE GLUE

Package condition: original