Soft copper sheet 30mm 200x100mm foiled

SLEEVE3.0CU200X100F Soft copper sheet with protective foil - length 200mm - width 100mm, thickness 3.0mm Copper sheet grade M1eR with a smooth surface can be polished to a mirror surface, is weldable and solderable, suitable for machining, perfectly conducts heat and electricity.

The sheet is covered on both sides with a foil that protects its surface from all scratches and dirt.

Element type: sheet with protective foil

Material: copper

Dimensions: 200x100mm

Thickness: 3.0mm

Structure: smooth surface

Grade: M1E

State of hardening: soft

Unit of measure: pcs.

Weight: 0.53kg

Copper sheet grade M1E, referred to in the European standard as CuETP, is mainly used in the electrical and electrical engineering industry. Thanks to its 99.99% copper content, it provides excellent conductivity. Copper sheet is mainly used to produce parts that serve as current conductors.

Cu-ETP - copper produced in the electrolytic refining process - cathodic melted. It is characterized by high thermal and electrical conductivity, has high plasticity and impact strength. Cu-ETP copper is susceptible to plastic processing (especially in the annealed state), it is susceptible to welding, brazing and soldering. Cu-ETP copper is very often used in industry - especially in the production of electrical and electronic components, in the production of cables and wires and in engineering applications.

Copper markings according to various standards:

EN: CW004A

ISO: Cu-ETP

DIN: E-Cu57/58

Wnr: 2.0060/2.0065

NFA FR: Cu-a1

UNS USA: C11000

BS GP old: C101

PN: M1E

Chemical composition of Cu-ETP (CW004A) (according to EN 573-1):

Cu : ≥99.9

Bi: ≤0.0005

O: ≤0.04

P: -

Pb: ≤0.005

Others total: ≤0.03

not included: Ag,O

Physical properties of Cu-ETP:

Density: 8.9 [g/cm3]

Melting point: 1083 [°C]

Specific heat at 20 °C: 394 [J/kgK]

Electrical conductivity: ≥100 [%IACS]

Thermal conductivity 390: [W/mK]

Young's modulus: 127 [GPa]

Thermal expansion coefficient at 20°C: 17.7 [10-6/K]

Strength properties of Cu-ETP R:

Tensile strength Rm: 220 [MPa]

Elongation A: 35 [%]

Conductivity: 58.5 MS/m

Hardness: 53 HV

Product code: 0BLACHA3.0CU200X100F