Aluminum sheet 50mm thick, size 250x250mm

BLACHA5.0AL250 Aluminum sheet - format - 250 x 250 mm, thickness 5.0 mmElement type: format

Material: aluminum

Dimensions: 250x250mm

Thickness: 5.0mm

Structure: smooth surface

Condition: raw aluminum

Grade: ENAW5754/PA11

State of hardening: H111

Unit of measure: piece

Weight: 830g

Format - aluminum sheet.

The aluminum alloy PA11/5754 is characterized by high corrosion resistance (also in contact with sea water). It has high fatigue strength, although average tensile strength. It is susceptible to plastic processing (especially in soft states). Suitable for welding, anodizing.

Aluminum designations PA11 (AW-5754) according to various standards:

EN: 5754

ISO: AlMg3

DIN: AlMg3

Wnr: 3.3535

NF FR: 5754

UNS: -

BS GP old: -

PN: PA11

Chemical composition ENAW5754/PA11 [%]:

Mg: 2.60 - 3.60

Mn: max 0.50

Fe: max 0.40

Si: max 0.40

Si+Fe: -

Cu: max 0.10

Zn: 0.20

Cr: max 0.30

Mn+Cr: 0.10 - 0.60

Ti: max 0.15

Bi: -

Ni: -

Pb: -

Sn: -

Zr: -

Zr+Ti: -

Others: max 0.05

Others together: max 0.15

Al: rest

Physical properties ENAW5754/PA11:

Density: 2.7 g/cm³

Solidification temperature: 595 °C

Pour point: 645 °C

Modulus of elasticity E: 70500 MPa

Transverse modulus of elasticity G: 26500 MPa

Poisson's ratio: 0.33

Specific heat: 897 J/kgK

Thermal expansion coefficient: 23.7 µm/mK

Specific resistance: 53 nWm

Thermal conductivity: 132 W/mK

Electrical conductivity: 32.5 %IACS

Strength properties of ENAW5754/PA11 with hardness state H111 and thickness 5mm (according to EN 485-2):

Tensile strength Rm min.: 190 [MPa]

Tensile strength Rm max.: 240 [MPa]

Yield strength Rp02 min.: 80 [MPa]

Yield strength Rp02 max.: - [MPa]

Min. elongation A50mm: 18 [%]

Min. elongation A: - [%]

Bending radius 180°: 1.0t

Bending radius 90°: 1.0t

Brinell hardness: 52 [HB]

Product code: 0BLACHA5.0AL250