Aluminum sheet 0.4mm thick, size 400x200mm

BLACHA0.4AL400x200 Aluminum sheet - format - 400 x 200 mm, thickness 0.4 mm, semi-hard Element type: format

Material: aluminum

Dimensions: 400x200mm

Thickness 0.4mm

Structure: smooth surface

Condition: raw aluminum

Grade: ENAW1050A/A1 H24/A1 Z4R

State of hardening: semi-hard

Unit of measure: piece

Weight: 90g

Format - aluminum sheet.

Aluminum alloy A1/1050A is characterized by high thermal and thermal conductivity. It is resistant to corrosion. It has considerable plasticity and is susceptible to cold forming. Suitable for welding, anodizing, polishing. Not suitable for machining.

Aluminum designations A1 (AW-1050A) according to various standards:

EN: 1050A

ISO: Al99.5

DIN: Al99.5

Wnr: 3.0255

NF FR: 1050A

UNS: A91050

BS GP old: 1B

PN: A1

Chemical composition A1/1050A [%]:

Si: max 0.25

Fe: max 0.40

Cu: max 0.05

Mn: max 0.05

Mg: max 0.05

Zn: max 0.07

Ti: max 0.05

Cr: -

Ni: -

Zr: -

Si+Fe: -

Mn+Cr: -

Bi: -

Pb: -

Sn: -

Zr+Ti : -

Other : max 0.03

Other together: max 0.15

Al: rest

Physical properties A1/1050A:

Density: 2.7 g/cm³

Solidification point: 645 °C

Pour point: 658 °C

Modulus of elasticity E: 69000 MPa

Transverse modulus of elasticity G: 25900 MPa

Poisson's number: 0.33

Specific heat: 899 J/kgK

Thermal expansion coefficient: 23.5 µm/mK

Specific resistivity: 29 nWm

Thermal conductivity: 229 W/mK

Electrical conductivity: 59.5 %IACS

Strength properties of 1050A with hardness state H24 and thickness 0.4mm (in accordance with EN 485-2):

Tensile strength Rm min.: 105 [MPa]

Tensile strength Rm max.: 145 [MPa]

Yield strength Rp02 min.: 75 [MPa]

Yield strength Rp02 max.: - [MPa]

Min. elongation A50mm: 3 [%]

Min. elongation A: - [%]

Bending radius 180°: 1.0t

Bending radius 90°: 0t

Brinell hardness: 33 [HB]