SHEET METAL 0 3AL400x200 Aluminum sheet 400x200mm thick 0 3

BLACHA0.3AL400x200 Aluminum sheet - format - 400 x 200 mm, thickness 0.3 mm, semi-hardElement type: format

Material: aluminum

Dimensions: 400x200mm

Thickness 0.3mm

Structure: smooth surface

Condition: raw aluminum

Grade: ENAW1050A/A1 H24/A1 Z4R

State of hardening: semi-hard

Unit of measure: piece

Weight: 60g

Format - aluminum sheet.

Aluminum alloy A1/1050A is characterized by high thermal and thermal conductivity. It is resistant to corrosion. It has considerable plasticity and is susceptible to cold forming. Suitable for welding, anodizing, polishing. Not suitable for machining.

Aluminum designations A1 (AW-1050A) according to various standards:

EN: 1050A

ISO: Al99.5

DIN: Al99.5

Wnr: 3.0255

NF FR: 1050A

UNS: A91050

BS GP old: 1B

PN: A1

Chemical composition A1/1050A [%]:

Si: max 0.25

Fe: max 0.40

Cu: max 0.05

Mn: max 0.05

Mg: max 0.05

Zn: max 0.07

Ti: max 0.05

Cr: -

Ni: -

Zr: -

Si+Fe: -

Mn+Cr: -

Bi: -

Pb: -

Sn: -

Zr+Ti : -

Others : max 0.03

Others together: max 0.15

Al: rest

Physical properties A1/1050A:

Density: 2.7 g/cm³

Solidification temperature: 645 °C

Pour point: 658 °C

Modulus of elasticity E: 69000 MPa

Modulus of transverse elasticity G: 25900 MPa

Poisson's ratio: 0.33

Specific heat: 899 J/kgK

Thermal expansion coefficient: 23.5 µm/mK

Specific resistivity: 29 nWm

Thermal conductivity: 229 W/mK

Conductivity electrical: 59.5 %IACS

Strength properties 1050A with hardening state H24 and thickness 0.3mm (according to EN 485-2):

Tensile strength Rm min.: 105 [MPa]

Tensile strength Rm max.: 145 [MPa]

Yield strength Rp02 min.: 75 [MPa]

Yield strength Rp02 max.: - [MPa]

Min. elongation A50mm: 3 [%]

Min. elongation A: - [%]

Bending radius 180°: 1.0t

Bending radius 90°: 0t

Brinell hardness: 33 [HB]

Product code: 0BLACHA0.3AL400X200